    2. Grade C27000

    ASTM F468/F468M Grade C27000 270 Brass Fasteners

    High quality ASTM F468 Brass fasteners manufactured for industrial and corrosion resistant applications.

    ASTM F468/F468M Grade C27000 Brass fasteners are manufactured in accordance with ASTM specifications for nonferrous bolts, hex cap screws, socket head cap screws, and studs.

    Chemical Requirements

    UNS Designation Number Alloy General Name Al Cu, min Fe,max Mn,max Ni,max P Si Zn, max A Pb,max Tin As,max
    Grade C27000 270 brass . . . 63.0-68.5 0.07 . . . . . . . . . . . . balance 0.10 . . . . . .
    • (A) Elements shown as balance shall be arithmetically computed by deducting the sum of the other named elements from 100.
    • (B) Copper plus specified elements = 99.8 min; copper plus silver = 88.5-91.5.
    • (C) Cobalt is to be counted as nickel.
    • (D) Minimum content of copper plus all other elements with specified limits shall be 99.5 %.
    • (E) An alloy containing as high as 2.6 % silicon is acceptable provided the sum of all the elements other than copper, silicon, and iron does not exceed 0.30 %.

    Mechanical Requirements

    Alloy Mechanical Property Marking Nominal Thread Diameter, in. Hardness A Full-Size Tests B Machined Specimen Tests
    Tensile Strength, ksi Yield Strength, min, ksi C Tensile Strength, min, ksi Yield Strength min, ksi C Elongation in 4D, min, % D
    Alloy Cu 270 F468B All 55-80 HRB 60-90 50 55 50 35
    • (A) Where both tension and hardness tests are performed, the tension tests shall take precedence for acceptance purposes. For aluminum and titanium alloys, hardness tests are for information only. See 6.5.
    • (B) The yield and tensile strength values for full-size products shall be computed by dividing the yield and maximum tensile load by the stress area for the product diameter and thread pitch as given in table on tensile stress areas.
    • (C) Yield strength is the stress at which an offset of 0.2 % gage length occurs.
    • (D) Elongation is determined using a gage length of 4 diameters of test specimen in accordance with Test Methods E8/E8M.
    • (E) "HF" denotes a hot-formed product.
    • (F) Aluminum alloy temper designations are in accordance with ANSI H35.1.
    • (G) Full-size test mechanical properties apply to fasteners with a maximum diameter of 76 mm. Mechanical properties of larger sections shall be negotiated between the material manufacturer and the fastener producer.
    • (H) Ti 5 Class A requires wedge tensile testing in accordance with Ti 5 Class B requires wedge tensile testing in accordance.

    ASTM F468/F468M Grade C27000 270 Brass Tensile Stress Areas and Threads(Inch)

    Nominal Size, in. Coarse Threads-UNC Fine Threads-UNF 8 Thread Series-8UN
    Threads/ in. Stress Area A , in. 2 Threads/ in. Stress Area A , in. 2 Threads/ in. Stress Area A , in. 2
    1 / 4 20 0.0318 28 0.0364 . . . . . .
    5 / 16 18 0.0524 24 0.0580 . . . . . .
    3 / 18 16 0.0775 24 0.0878 . . . . . .
    7 / 16 14 0.1063 20 0.1187 . . . . . .
    1 / 2 13 0.1419 20 0.1599 . . . . . .
    9 / 16 12 0.1820 18 0.2030 . . . . . .
    5 / 8 11 0.2260 18 0.2560 . . . . . .
    3 / 4 10 0.3340 16 0.3730 . . . . . .
    7 / 8 9 0.4620 14 0.5090 . . . . . .
    1 8 0.6060 12 0.6630 . . . . . .
    1 1 / 8 7 0.7630 12 0.8560 8 0.790
    1 1 / 4 7 0.9690 12 1.0730 8 1.000
    1 3 / 8 6 1.1550 12 1.3150 8 1.233
    1 1 / 2 6 1.4050 12 1.5810 8 1.492
    • (A) Tensile stress areas are computed using the following formula:
    • A s = 0.7854 [ D - 0.9743/n ]
    • where:
    • As = tensile stress area, in.2,
    • D = nominal size (basic major diameter), in., and
    • n = number of threads per inch.

    ASTM F468/F468M Grade C27000 270 Brass Tensile Stress Areas (Metric)

    Nominal Product Diameter and Thread Pitch Stress Area, A mm 2 Nominal Product Diameter and Thread Pitch Stress Area, A mm 2
    M6 × 1 20.1 M16 × 2 157
    M8 × 1.25 36.6 M20 × 2.5 245
    M10 × 1.5 58.0 M24 × 3 353
    M12 × 1.75 84.3 M30 × 3.5 561
    M14 × 2 115 M36 × 4 817
    • (A) Tensile stress areas are computed using the following formula:
    • A s = 0.7854 (D − 0.9382 P) 2
    • where:
    • As = stress area, mm2,
    • D  = nominal thread diameter, mm, and
    • P  = thread pitch, mm.

    Frequently Asked Questions

    What is Brass C27000 (Yellow Brass)?

    Brass C27000 is a 65/35 Cu-Zn yellow brass per ASTM F468 - slightly stronger than cartridge brass C26000 (more Zn) with similar cold-formability. Tensile 49-85 ksi depending on temper. General-purpose brass alternative when C26000's properties don't quite match the design need.

    When use C27000 over C26000?

    C27000 is slightly cheaper than C26000 and slightly stronger - choose when small strength gain matters and color match between C27000 and C26000 hardware is acceptable. C27000 is more dezincification-susceptible than C26000 in marine service.

    Marine service guidance?

    Neither C26000 nor C27000 is recommended for seawater bolting - both can dezincify rapidly. For marine service use naval brass C46400 (Cu-Zn-Sn) or nickel-aluminum bronze C63000.

    Available dimensional patterns?

    Same as C26000 - ASME B18.2.1 hex bolts, B18.5 round head, B18.6.7M metric machine screws.

    References & Standards

    • ASTM F468 / F468M - Standard Specification for Nonferrous Bolts, Hex Cap Screws, and Studs for General Use
    • ASTM F467 / F467M - Companion specification for Nonferrous Nuts (mate with F468 for matched-alloy assemblies)
    • ASTM F436 / F436M - Hardened steel washers (ferrous washer companion when nonferrous washers are not specified)
    • NACE MR0175 / ISO 15156 - Sour-service hardness limits for petroleum and natural gas industries
    • ASME B18.2.1 / B18.2.3 series / B18.3 / B18.6.7M / B18.31 / B16.5 - Dimensional standards referenced by F468
    • DIN 912 / 933 / 931 - Metric hex socket head and hex head cap screw dimensional standards
    Related Specifications
    Surface Treatments
    Certifications
    About Us
    Questions? Contact us.
    Showcase of our Microsites.
    Satisfaction Survey

    survey

    TUVRheinland CERTIFIED

    © TorqBolt P(Ltd) · Built with in INDIA.